Title

UTILIZAÇÃO DE PELOTAS AUTO-REDUTORAS NA PRODUÇÃO DE FERROLIGAS (FERROCROMO ALTO CARBONO)

UTILIZATION OF THE SELF-REDUCING AGGLOMERATES FOR THE FERROALLOYS PRODUCTION (FERRO-CHROMIUM HIGH CARBON)

Authorship

Zambrano, Adolfo Pillihuaman; Nogueira, Alberto Eloy Anduze; Takano, Cyro; Mourão, Marcelo Breda

Zambrano, Adolfo Pillihuaman

I am this author

Nogueira, Alberto Eloy Anduze

I am this author

Takano, Cyro

I am this author

Mourão, Marcelo Breda

I am this author

DOI

10.5151/2594-357x-12836

Downloads

Abstract

Aglomerados auto-redutores têm-se mostrado eficientes na redução de cromitas para produção de ferro-cromo alto carbono (FeCrAC), seja melhorando a velocidade de redução, seja aumentando o rendimento de recuperação de cromo e seja economizando energia elétrica. Pelotas auto-redutoras da cromita brasileira contendo coque de petróleo e ~2% de Fe-75%Si, aglomeradas com cimento Portland com e sem adição de fluxantes (SiO2 e CaO), foram ensaiadas a 1773K até que não houvesse evolução dos gases de redução. O produto resultante foi analisado por microscopia eletrônica e a composição das fases presentes por EDS. Neste trabalho é mostrado que a adição de fluxantes na composição das pelotas auto-redutoras de cromita antes de serem reduzidas origina formação de uma fase escória, dificultando a velocidade de redução. Os resultados mostraram que aglomerados auto-redutores sem adição de fluxantes a velocidade de redução foi 2 vezes mais rápida comparados com os contendo fluxantes, a 1773K.. Isto confirma a importância do mecanismo de reação gás-sólido na redução carbotérmica da cromita. Tendo em vista os resultados, foi solicitado o devido pedido de prioridade.

Fe-Cr-C production is a very high electrical energy consuming process. When self- reducing agglomerates are used it is expected to decrease up to 10% this electrical energy. Self-reducing pellets of the Brazilian chromites containing petroleum coke and ~2% Fe-75%Si were agglomerated using Portland cement as the binder with and without fluxing additions (CaO + SiO2). The pellets were dried and submitted at temperature of 1773K up to complete the reactions. The resulting products were analyzed by Scanning Electron Microscopy and by microanalysis (XEDS). The results showed that when only small quantity of slag is formed the reduction rate is much faster, confirming that when slag is formed the chromites particles would be covered by the slag and the reaction mechanism will change from fast gas/solid reaction to slower one slag/metal reaction rate In the experiments when a continuous and dense slag was formed, due to fluxing agents addition, the reduction rate was as much twice slower than that of agglomerates which only a small quantity of the slag was formed. These results confirm the importance the gas/solid reaction of the carbothermic reduction of the chromites. The request for priority was applied.