UTILIZAÇÃO DO RESÍDUO DE VIDRO PARA O DESENVOLVIMENTO DE TELHAS GEOPOLIMÉRICAS

DEVELOPMENT OF GEOPOLIMERIC ROOF TILES USING GLASS WASTE

Authorship

MELLO, THEREZA PEREIRA RAMOS DE; CRUZ, LUCAS REIS; JÚNIOR, DAVI VAZ ANDRÉ; OLIVEIRA, LEANDRO BARBOSA DE; BARRAZA, MADELEING TABORDA; VIEIRA, CARLOS MAURÍCIO FONTES; AZEVEDO, AFONSO RANGEL GARCEZ DE

MELLO, THEREZA PEREIRA RAMOS DE

I am this author

CRUZ, LUCAS REIS

I am this author

JÚNIOR, DAVI VAZ ANDRÉ

I am this author

OLIVEIRA, LEANDRO BARBOSA DE

I am this author

BARRAZA, MADELEING TABORDA

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

AZEVEDO, AFONSO RANGEL GARCEZ DE

I am this author

DOI

10.5151/2594-4711-40598

Downloads

Abstract

A NORMA BRASILEIRA ESTIPULA UM PADRãO DE QUALIDADE PARA AS TELHAS CERâMICAS, FAZENDO QUE MUITOS PRODUTOS SEJAM DESCARTADOS POR NãO CUMPRIREM O NíVEL REQUERIDO, O QUE ACENTUA O IMPACTO AMBIENTAL LOCAL, AUMENTANDO A QUANTIDADE DE RESíDUOS DE MODO INVOLUNTáRIO. LOGO, ESTE TRABALHO VISA ESTUDAR A INCORPORAçãO DE RESíDUO DE VIDRO, PARA ELABORAçãO FUTURA DE TELHAS GEOPOLIMéRICAS. FORAM ELABORADAS COMPOSIçõES DE REFERêNCIA, DE 10%, 20% E 30% DE ADIçãO DO RESíDUO DE VIDRO, ORIUNDO DA LAPIDAçãO DE VIDROS PLANOS, E POSTERIORMENTE FOI AVALIADA A RESISTêNCIA DE COMPRESSãO EM 7 E 28 DIAS. OUTROS PARâMETROS COMO íNDICE DE CONSISTêNCIA, DENSIDADE NO ESTADO ENDURECIDO, ABSORçãO DE áGUA POR IMERSãO E íNDICE DE VAZIOS TAMBéM FORAM ESTUDADOS PARA MAIOR ANáLISE DA ARGAMASSA GEOPOLíMERICA. OS RESULTADOS DEMONSTRARAM QUE, INCORPORANDO 20% DO RESíDUO PODERIA SER ATINGIDA UMA RESISTêNCIA à COMPRESSãO DE 30MPA PARA UMA AMOSTRA EM TEMPERATURA CONTROLADA DURANTE 28 DIAS. LOGO, O MATERIAL PESQUISADO APRESENTA GRANDE POTENCIAL DE USO, PORéM AINDA é NECESSáRIO MAIS INVESTIGAçõES PARA A DETERMINAçãO DA EFICIêNCIA COMPLETA DO MATERIAL.

THE BRAZILIAN STANDARD STIPULATES A QUALITY STANDARD FOR CERAMIC ROOF TILES, CAUSING MANY PRODUCTS TO BE DISCARDED BECAUSE THEY DON´T MATCH THE REQUIRED LEVEL, WHICH ACCENTUATES THE LOCAL ENVIRONMENTAL IMPACT, UNINTENTIONALLY INCREASING THE AMOUNT OF WASTE. THEREFORE, THIS WORK AIMS TO STUDY THE INCORPORATION OF GLASS WASTE FOR THE FUTURE PRODUCTION OF GEOPOLYMERIC ROOF TILES. REFERENCE COMPOSITIONS WERE PREPARED, WITH 10%, 20% AND 30% ADDITION OF GLASS RESIDUE, ORIGINATING FROM THE CUTTING OF FLAT GLASS, AND SUBSEQUENTLY THE COMPRESSIVE STRENGTH WAS EVALUATED AT 7 AND 28 DAYS. OTHER PARAMETERS SUCH AS CONSISTENCY INDEX, DENSITY IN THE HARDENED CONDITION, WATER ABSORPTION BY IMMERSION AND VOID INDEX WERE ALSO STUDIED FOR FURTHER ANALYSIS OF THE GEOPOLYMER MORTAR. THE RESULTS DEMONSTRATED THAT, INCORPORATING 20% OF THE RESIDUE, A COMPRESSIVE STRENGTH OF 30MPA COULD BE ACHIEVED FOR A SAMPLE AT A CONTROLLED TEMPERATURE FOR 28 DAYS. THEREFORE, THE RESEARCHED MATERIAL HAS GREAT POTENTIAL FOR USE, BUT FURTHER INVESTIGATION IS STILL NEEDED TO DETERMINE THE COMPLETE EFFICIENCY OF THE MATERIAL.