AVALIAÇÃO COMPARATIVA DO DESGASTE DE HÉLICES INTEIRIÇAS E TRIPARTIDAS EM ASTM A36 REVESTIDAS COM AS LIGAS CDP 4666 E CDP 4668 EM CLASSIFICADORES ESPIRAIS

COMPARATIVE EVALUATION OF WEAR IN SOLID AND TRIPARTITE HELICES IN ASTM A36 COATED WITH CDP 4666 AND CDP 4668 ALLOYS IN SPIRAL CLASSIFIERS

Authorship

BARROS, VANESSA GONÇALVES DE ALMEIDA; DOMINGUES, MARLON LOUSADA; TEIXEIRA, WARLEY ETIENE NONATO; MARTINS, AMANDA CAROLINA MOREIRA; FERREIRA, MARIA MARIANA SIMÕES

BARROS, VANESSA GONÇALVES DE ALMEIDA

I am this author

DOMINGUES, MARLON LOUSADA

I am this author

TEIXEIRA, WARLEY ETIENE NONATO

I am this author

MARTINS, AMANDA CAROLINA MOREIRA

I am this author

FERREIRA, MARIA MARIANA SIMÕES

I am this author

DOI

10.5151/2594-5327-42692

Downloads

Abstract

O desempenho de hélices de classificadores espirais é crucial para a eficiência operacional em plantas de processamento mineral, devido ao ambiente altamente abrasivo que enfrentam (MTBF). Esta condição reduz sua vida útil e eleva custos e tempo de manutenção. Este estudo avaliou a viabilidade técnico-operacional de hélices em aço ASTM A36 revestidas por soldagem, usando duas ligas: CDP 4666 na hélice inteiriça e CDP 4668 no modelo tripartido. Os testes na Usina da Mutuca incluíram inspeções periódicas para monitoramento do desgaste e perda de massa. Os resultados mostraram que a liga CDP 4668 teve menor taxa de desgaste, devido à presença de vanádio e tungstênio, que formam carbonetos de maior dureza e estabilidade. Observou-se também uma redução no tempo de substituição das hélices (tempo médio de reparo - MTTR), de 3,5 horas para 1,5 horas. A análise de custo-benefício revelou uma economia anual de 53%, além de aumento na vida útil dos componentes. Conclui-se que a hélice tripartida revestida com CDP 4668 é superior à CDP 4666 para operações de classificação de minério em ambientes de alto desgaste abrasivo.

The performance of spiral classifier blades is crucial for operational efficiency in iron ore processing plants due to the highly abrasive environment they operate. This condition reduces their service life and increases maintenance costs and the mean time between failures (MTBF). This study evaluated the technical-operational feasibility of ASTM A36 steel blades coated by welding, using two alloys: CDP 4666 in one-piece blade and CDP 4668 in a segmented 3-parts model. Tests conducted at Mutuca Industrial Plant included periodic inspections to monitor wear and mass loss. Results showed that the CDP 4668 alloy exhibited a lower wear rate, due to the presence of vanadium and tungsten, which form harder and more stable carbides. A reduction in blade replacement time (mean time to repair -MTTR) was also observed, from 3.5 hours to 1.5 hours. The cost-benefit analysis revealed an annual savings of 53%, along with increased component service life. It is concluded that the segmented blade coated with CDP 4668 exceeded CDP 4666 for ore classification operations in high-abrasion environments.