Estudo da incorporação do pó calcinado de conchas de caramujo africano (Achatina fulica) em argamassa de revestimento no estado endurecido

Study on the incorporation of calcined African giant land snail shell powder (Achatina fulica) in rendering mortar at the Hardened state

Authorship

TAVARES, ESTHER; SANTOS, MANOEL TADEU ALVES DOS; PEREIRA, IULLY DA SILVA AMARAL; FREITAS, JOHNATA FRANÇA FANNI; JÚNIOR, ELIAS ROCHA GONÇALVES; FONSECA, LARISSA MENDONÇA OSORIO; AZEVEDO, AFONSO RANGEL GARCEZ DE

TAVARES, ESTHER

I am this author

SANTOS, MANOEL TADEU ALVES DOS

I am this author

PEREIRA, IULLY DA SILVA AMARAL

I am this author

FREITAS, JOHNATA FRANÇA FANNI

I am this author

JÚNIOR, ELIAS ROCHA GONÇALVES

I am this author

FONSECA, LARISSA MENDONÇA OSORIO

I am this author

AZEVEDO, AFONSO RANGEL GARCEZ DE

I am this author

DOI

10.5151/2594-4711-43092

Downloads

Abstract

A busca por soluções sustentáveis na área da construção civil tem incentivado o reaproveitamento de resíduos com potencial de aplicação em matrizes cimentícias. Nesse contexto, este trabalho avaliou o desempenho de argamassas de revestimento com a incorporação de pó calcinado de conchas do caramujo gigante terrestre africano (Achatina fulica) em teores de 1%, 2% e 3%. O resíduo foi coletado, processado, peneirado e calcinado a 1000 °C por 1 hora, sendo posteriormente incorporado a argamassas com traço 1:1:6. Os corpos de prova foram submetidos a ensaios de difratômetria de Raios-X, densidade de massa, resistência à tração na flexão e resistência à compressão, após 7 dias de cura. Os resultados indicaram alterações mineralógicas decorrentes da calcinação, com redução dos picos de carbonato de cálcio e surgimento de fases associadas ao hidróxido de cálcio. Também foi observada leve redução da densidade de massa com o aumento do teor incorporado, sem prejuízo significativo do desempenho mecânico. As resistências à flexão e à compressão permaneceram próximas às da argamassa de referência, demonstrando compatibilidade técnica do resíduo em baixos teores. Dessa forma, pôde-se concluir que o pó calcinado apresenta potencial de uso como adição sustentável em argamassas de revestimento.

The search for sustainable solutions in the civil construction sector has encouraged the reuse of waste materials with potential application in cementitious matrices. In this context, this study evaluated the performance of rendering mortars incorporating calcined powder derived from shells of the African giant land snail (*Achatina fulica*) at contents of 1%, 2%, and 3%. The waste material was collected, processed, sieved, and calcined at 1000 °C for 1 hour, and subsequently incorporated into mortars with a 1:1:6 mix proportion. Specimens were subjected to X-ray diffraction, bulk density, flexural tensile strength, and compressive strength tests after 7 days of curing. The results indicated mineralogical changes resulting from calcination, including a reduction in calcium carbonate peaks and the emergence of phases associated with calcium hydroxide. A slight decrease in bulk density was also observed with increasing incorporation levels, without significant impairment of mechanical performance. Flexural and compressive strengths remained close to those of the reference mortar, demonstrating the technical compatibility of the residue at low incorporation levels. Therefore, it was concluded that calcined shell powder presents potential for use as a sustainable additive in rendering mortars.

Keywords

Argamassa, Estado Endurecido, Caramujo africano, Achatina fulica, Pó de conchas, Calcinação, Resíduo biológico, Sustentabilidade

Mortar, Hardened state, African snail, Achatina fulica, Shell powder, Calcination, Biological waste, Sustainability