Anais do Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas


ISSN 2594-4711

Título

ANÁLISE DAS PROPRIEDADES TECNOLÓGICAS DE REVESTIMENTOS CERÂMICOS FABRICADOS COM ARGILA CAULINÍTICA DE BOA SAÚDE-RN

ANALYSIS OF THE TECHNOLOGICAL PROPERTIES OF CERAMIC COATINGS MANUFACTURED WITH CAULINÍTIC CLAY OF BOA SAÚDE - RN

DOI

10.5151/2594-4711-33902

Downloads

Baixar Artigo 4 Downloads

Resumo

As argilas são matérias primas fundamentais na confecção dos produtos cerâmicos. Na produção de revestimentos cerâmicos as argilas com baixa quantidade de óxido ferro (Fe2O3), que resultam em peças com coloração branca ou bege, são preferenciais. Esse tipo de argila não é comumente encontrado pela indústria, o que torna seu valor expressivamente mais alto. Portanto, o objetivo deste trabalho é analisar as propriedades tecnológicas de massas cerâmicas produzidas com uma argila caulinítica do município de Boa Saúde-RN para produção de revestimentos. O procedimento experimental teve início com a fabricação das massas cerâmicas usando a argila, quartzo, caulim, feldspato K e dolomita, todos materiais com granulometria de 0,074mm. O processo de compactação das amostras ocorreu em uma prensa hidráulica com pressão de 21 MPa. As peças foram secas em uma estufa e sinterizadas no forno do tipo mufla, sem atmosfera protetora, nas temperaturas de 1000°C e 1100°C, com taxa de aquecimento de 10°C/min e patamar de isoterma de 60 minutos. No total, foram confeccionadas quarenta (40) amostras, sendo vinte (20) por temperatura. As propriedades tecnológicas das amostras foram aferidas através dos ensaios de absorção de água (AA%), retração linear (RL%), perda ao fogo (PF%), porosidade aparente (PA%) e massa específica aparente (MEA). Os resultados dos ensaios apontam que a argila estudada pode ser destinada para o setor de revestimentos do tipo poroso.

 

Clays are fundamental raw materials in the manufacture of ceramic products. In the production of ceramic tiles, low iron oxide (Fe2O3) clays, which result in white or beige colored pieces, are preferred. This type of clay is not commonly found by industry, which makes its value significantly higher. Therefore, the objective of this work is to analyze the technological properties of ceramic masses produced with a kaolinitic clay from the city of Boa Saúde-RN for the production of coatings. The experimental procedure began with the manufacture of the ceramic masses using clay, quartz, kaolin, feldspar K and dolomite, all materials with 0.074mm particle size. The sample compaction process took place on a 21 MPa pressure hydraulic press. The pieces were dried in an oven and sintered in the muffle furnace, without protective atmosphere, at temperatures of 1000°C and 1100°C, with heating rate of 10°C/min and isotherm level of 60 minutes. Forty (40) samples were made, twenty (20) per temperature. The technological properties of the samples were measured by water absorption (AA%), linear shrinkage (RL%), fire loss (PF%), apparent porosity (PA%) and apparent specific mass (MEA) tests. The results of the tests indicate that the studied clay can be destined for the porous type coatings sector.

Palavras-chave

Argila; Boa Saúde; Rio Grande do Norte; Revestimentos Cerâmicos.

Clay; Boa Saúde; Rio Grande do Norte; Ceramic coatings.

Como citar

Costa, Anna Beatriz Almeida Leandro da; Souza, Bruna Pereira do Nascimento; Ribeiro Neto, Djalma Valério; Meyer, Mauro Froes; Monteiro, Flánelson Maciel. ANÁLISE DAS PROPRIEDADES TECNOLÓGICAS DE REVESTIMENTOS CERÂMICOS FABRICADOS COM ARGILA CAULINÍTICA DE BOA SAÚDE-RN , p. 151-160. In: 19° Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas (ENEMET), São Paulo, 2019.