AVALIAÇÃO DA CORROSÃO INTERGRANULAR NO AÇO AISI 304L PELA NORMA ASTM A262, PRÁTICAS A, C E E

EVALUATION OF INTERGRANULAR CORROSION ON STEEL AISI 304L BY METHOD ASTM A262, PRACTICE A, C AND E

DOI

10.5151/1516-392X-27071

Downloads

Baixar Artigo 3653 Downloads

Resumo

Os aços inoxidáveis austeníticos apresentam interessante junção de propriedade mecânica com elevada resistência à corrosão. Porém, quando aplicados em temperaturas na faixa de sensitização e submetidos a ambientes agressivos, tornam-se suscetíveis à corrosão intergranular. Para verificação da suscetibilidade desses aços sofrem este fenômeno são realizados ensaios de corrosão. Dentre eles os mais utilizados são os contidos na norma ASTM A262, que possui cinco diferentes procedimentos. Este trabalho consiste na comparação dos procedimentos das Práticas A, C e E, contidos nessa norma, para determinação da tendência à corrosão intergranular do aço AISI 304L. Para isto, amostras do aço foram sensitizadas a 675°C por uma hora e em seguida submetidas aos diferentes ensaios descritos na norma. Após a realização dos três procedimentos, considera-se que a metodologia mais assertiva e confiável seja a Prática E, conhecido como ensaio de Strauss, e que as amostras analisadas não apresentaram corrosão intergranular.

 

The austenitic stainless steels have interesting junction mechanical property with high corrosion resistance. However, when applied at temperatures in the range of sensitization and subjected to harsh environments, they become susceptible to intergranular corrosion. To verify the susceptibility of these steels suffer from this phenomenon corrosion tests are performed. Among them the most used are those contained in ASTM A262, which has five different procedures. This work consists in comparing the procedures of Practices A, C and E contained in this standard for determining the tendency to intergranular corrosion of steel AISI 304L. For this, the steel samples were sensitizadas at 675°C for one hour and then subjected to the various tests described in the standard. After completion of the three procedures, it is considered that the most assertive and reliable methodology is the Practice E, known as Strauss test, and the samples analyzed showed no intergranular corrosion.

Palavras-chave

AISI 304L, Corrosão intergranular, ASTM A262

AISI 304L, Intergranular corrosion, ASTM A262