AVALIAÇÃO DO COMPORTAMENTO MECÂNICO DA SUPERLIGA INCONEL 718 A 650°C SOB TENSÃO DE 510 A 625 MPa

EVALUATION OF MECHANICAL BEHAVIOR OF INCONEL 718 SUPERALLOY AT 650°C AND 510 AND 625 MPa

DOI

10.5151/2594-4711-23253

Downloads

Baixar Artigo 200 Downloads

Resumo

Durante a operação de um motor aeronáutico, os materiais utilizados são expostos a ambientes hostis devendo apresentar elevada resistência mecânica, boa resistência à fadiga, à fluência e à corrosão e capacidade de operar continuamente em elevadas temperaturas. Para entender o comportamento mecânico desses materiais são necessários ensaios que reproduzam as condições de operação desses motores. Para estudar o comportamento em fluência, a superliga Inconel 718 - material amplamente usado em motores aeronáuticos - foi submetida às tensões de 510 MPa e 625 MPa à temperatura constante de 650ºC. Com os resultados dos ensaios, foi determinada a curva com comportamento típico em fluência sendo observada uma dependência direta entre a tensão e a resistência à fluência, assim como o tempo de vida. A liga de Inconel 718 submetida ao ensaio de fluência na condição de menor tensão apresentou uma maior resistência à fluência do que a liga que foi submetida ao ensaio de fluência em uma condição de maior tensão. Pela observação da fratura sofrida pelo material, pode-se notar que o mecanismo de fratura atuante foi a fratura dúctil, com a presença de dimples e microcavidades de média profundidade.

 

During the operation of an aeronautical engine, materials are exposed to a hostile environment, for which they must present high mechanical resistance, good fatigue, creep and corrosion performance and capability to sustain continuous operation at high temperatures. To understand the mechanical performance of such materials, tests that emulate engine operational conditions are needed. To study its creep performance, Inconel 718 superalloy – a material largely used in aeronautical engines – was stress tested at 510 and 625 MPa at a constant 650ºC temperature. With the test results, a typical creep performance curve was determined, and a direct dependance between stress and creep resistance was observed, as well as lifetime. The Inconel 718 alloy test subject subjected to the creep test in the lower stress condition presented higher creep resistance than the one that was subjected to the higher stress condition. By observing the fracture presented by the material, one can notice that a ductile fracture mechanism occurred, presenting dimples and medium depth microcavities.

Palavras-chave

Inconel 718; Fluência; Temperaturas elevadas.

Inconel 718; Creep; High temperature.

Como citar

Neto, Fabiana de Souza; Gonçalves, Erika Peterson; Martinolli, Karina; Reis, Danieli Aparecida Pereira; Neto, Carlos de Moura. AVALIAÇÃO DO COMPORTAMENTO MECÂNICO DA SUPERLIGA INCONEL 718 A 650°C SOB TENSÃO DE 510 A 625 MPa , p. 253-258. In: 13º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo - Brasil, 2013.