AVALIAÇÃO EM ALTA TEMPERATURA DE BRIQUETES COMPOSTOS POR CAREPA E PÓ DE BALÃO

HIGH-TEMPERATURE EVALUATION OF BLAST FURNACE FLUE DUST AND MILL SCALE BRIQUETTES

DOI

10.5151/2594-4711-31944

Downloads

Baixar Artigo 221 Downloads

Resumo

Desenvolver novas matérias-primas e tecnologias que forneçam alternativas para o reaproveitamento de resíduos siderúrgicos é importante tanto do ponto de vista econômico quanto para a sustentabilidade do setor. Devido ao rico teor de ferro e carbono de alguns desses resíduos, a reciclagem via briquetes autorredutores em reatores de redução é uma rota considerada por diversos especialistas. No entanto, para consolidar tal aplicação, é fundamental conhecer o comportamento desses aglomerados em condições próximas daquelas presentes na prática industrial. O presente trabalho buscou avaliar o desempenho de aglomerados autorredutores compostos por pó de balão de alto-forno e carepa em altas temperaturas. Briquetes com diferentes proporções de pó de balão e carepa foram produzidos em laboratório, usando cimento e água como ligantes. Esses aglomerados foram submetidos a ensaios de redução não isotérmicos em atmosfera de CO/CO2 nas temperaturas de 300, 600, 900 e 1100°C e os produtos foram avaliados por meio de perda de massa e resistência mecânica. Os resultados obtidos mostraram as variações de resistência mecânica em função da perda de massa e das diferentes proporções de resíduos dos aglomerados. Por fim, visando o uso desses aglomerados em alto-forno, a melhor proporção entre pó de balão de alto-forno e carepa foi identificada.

 

Developing new technologies that provide alternative ways to reuse metallurgical waste is important for the industry and the environment. Due to the rich iron and carbon content of some of those wastes, many researchers suggested their potential for the production of self-reducing agglomerates targeted for reduction reactors. However, to consolidate such applications, it is fundamental to know the behavior of these agglomerates in conditions close to those present in the industrial practice. The present work aimed to evaluate the performance of self-reducing agglomerates composed of blast-furnace flue dust and mill scale at high temperatures. Briquettes with different proportions of blast furnace dust and mill scale were produced in laboratory scale, using cement and water as binders. These agglomerates were subjected to non-isothermal reduction tests in CO/CO2 atmosphere at temperatures of 300, 600, 900 and 1100°C and the products obtained were evaluated by mass loss and mechanical strength. The obtained results showed the variations of mechanical strength as a function of the mass loss and the different ratios of residues of the agglomerates. Finally, aiming to use such agglomerates at the blast furnace, the best ratio between blast furnace dust and mill scale was identified.

Palavras-chave

Resíduos Siderúrgicos; Autorredução; Pó de Balão; Carepa.

Metallurgical Waste; Self-Reduction; Blast Furnace Flue Dust, Mill Scale.