COM A AMPLIAçãO DAS REDES DE TRANSMISSãO (TX) E DISTRIBUIçãO (DX) DE ENERGIA ELéTRICA DEVIDO AO DESENVOLVIMENTO URBANO E O CONSTANTE CRESCIMENTO DO SETOR INDUSTRIAL, TORNA-SE NECESSáRIO VIABILIZAR MATERIAIS DE BAIXO CUSTO QUE PROPORCIONEM BOAS PROPRIEDADES PARA A FABRICAçãO DOS CABOS TX E DX. PORTANTO, ESTE ESTUDO TEVE COMO OBJETIVO ANALISAR A MACROESTRUTURA E AS PROPRIEDADES ELéTRICAS E MECâNICAS DA LIGA AL-0,5%SI, BEM COMO A INFLUêNCIA DA ADIçãO DE 0,3% DE NíQUEL (NI) E DO TRATAMENTO TéRMICO DE RECOZIMENTO. PARA A OBTENçãO DOS RESULTADOS, FOI REALIZADA A METALOGRAFIA, OS ENSAIOS DE RESISTêNCIA ELéTRICA E DE TRAçãO, LOGO OS RESULTADOS FORAM ANALISADOS E COMPARADOS. OS RESULTADOS EVIDENCIARAM QUE O NI PROVOCOU UM ALONGAMENTO NA ESTRUTURA CRISTALINA, ENQUANTO O RECOZIMENTO ALTEROU A ORIENTAçãO DOS GRãOS. A CONDUTIVIDADE ELéTRICA APRESENTOU UM AUMENTO PEQUENO DE 61% PARA 61,23% IACS NAS LIGAS NãO TRATADAS TERMICAMENTE, ENQUANTO O RECOZIMENTO ELEVOU A PROPRIEDADE PARA 67,99% IACS. PARA OS RESULTADOS DE RESISTêNCIA à TRAçãO EVIDENCIARAM UM AUMENTO DE 185 PARA 254,25 MPA COM A ADIçãO DO NI, PORéM APóS O RECOZIMENTO HOUVE UMA DIMINUIçãO PARA 93,30 MPA. PORTANTO, VERIFICOU-SE QUE A ADIçãO DO NI MODIFICOU A ESTRUTURA E AFETOU DE FORMA SIGNIFICATIVA A RESISTêNCIA DO MATERIAL E O RECOZIMENTO CONTRIBUIU PARA O APRIMORAMENTO DA CONDUTIVIDADE ELéTRICA.
WITH THE EXPANSION OF TRANSMISSION (TX) AND DISTRIBUTION (DX) NETWORKS FOR ELECTRICAL ENERGY DUE TO URBAN DEVELOPMENT AND THE CONSTANT GROWTH OF THE INDUSTRIAL SECTOR, IT BECOMES NECESSARY TO ENABLE LOW-COST MATERIALS THAT PROVIDE GOOD PROPERTIES FOR THE MANUFACTURING OF TX AND DX CABLES. THEREFORE, THIS STUDY AIMED TO ANALYZE THE MACROSTRUCTURE AND THE ELECTRICAL AND MECHANICAL PROPERTIES OF THE AL-0,5%SI ALLOY, AS WELL AS THE INFLUENCE OF ADDING 0,3% NICKEL (NI) AND ANNEALING HEAT TREATMENT. METALLOGRAPHY, ELECTRICAL RESISTANCE, AND TENSILE TESTS WERE CONDUCTED TO OBTAIN THE RESULTS, WHICH WERE SUBSEQUENTLY ANALYZED AND COMPARED. THE RESULTS SHOWED THAT NI CAUSED ELONGATION IN THE CRYSTAL STRUCTURE, WHILE ANNEALING ALTERED THE GRAIN ORIENTATION. ELECTRICAL CONDUCTIVITY SHOWED A SMALL INCREASE FROM 61% TO 61,23% IACS IN UNTREATED ALLOYS, WHILE ANNEALING RAISED THE PROPERTY TO 67,99% IACS. TENSILE STRENGTH RESULTS EVIDENCED AN INCREASE FROM 185 TO 254,25 MPA WITH THE ADDITION OF NI, BUT AFTER ANNEALING, THERE WAS A DECREASE TO 93,30 MPA. THEREFORE, IT WAS FOUND THAT THE ADDITION OF NI MODIFIED THE STRUCTURE AND SIGNIFICANTLY AFFECTED THE MATERIAL'S STRENGTH, AND ANNEALING CONTRIBUTED TO THE ENHANCEMENT OF ELECTRICAL CONDUCTIVITY.
Palavras-chave
Al-Si-Ni; Elemento de liga; Condutividade; Tratamento térmico.
Al-Si-Ni; Alloying element; Conductivity; Heart treatment.
Como citar
BARBOSA, ALICIA REGINA ZANON;
ARAÚJO, YAN CHRISTIAN SILVA DE;
ESPÍNDOLA, ERIC ELIAN LIMA;
MARQUES, LUANE LUIZA PEREIRA;
SILVA, MARIA ADRINA PAIXÃO DE SOUZA DA;
MEDEIROS, AMANDA LUCENA DE;
COSTA, DEIBSON SILVA DA.
CARACTERIZAÇÃO E AVALIAÇÃO DA LIGA AL-05%SI E A INFLUÊNCIA DA ADIÇÃO DE 0,3% DE NÍQUEL E RECOZIMENTO
,
p. 266-277.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-40920