CARACTERIZAÇÃO TECNOLÓGICA E TRATAMENTO DE UM REJEITO GROSSO DE MINÉRIO DE FERRO POR CONCENTRAÇÃO MAGNÉTICA DE ALTA INTENSIDADE

TECHNOLOGICAL CHARACTERIZATION AND TREATMENT OF A THICK IRON ORE REJECT BY A HIGH INTENSITY MAGNETIC CONCENTRATION

DOI

10.5151/2594-357X-31562

Downloads

Baixar Artigo 249 Downloads

Resumo

A unidade Arcelor Mittal Mineração Serra Azul gera um rejeito do processo de jigagem, durante a concentração de minério de ferro do tipo sinter feed. Esse material é empilhado e não comercializado devido às características que não se adequam aos padrões de qualidade definidos pelo mercado siderúrgico. O presente estudo propõe a caracterização tecnológica desse rejeito, através das técnicas de classificação granulométrica, fluorescência de raios X, difração de raios X e microscopia óptica. Posteriormente, propõe-se a rota de concentração magnética de alta intensidade em etapa rougher para três faixas granulométricas distintas. Amostra A- (-5,00mm+2,36mm), Amostra B- (-2,36mm+0,60mm) e Amostra C- (-0,60mm). Após os ensaios de concentração, os valores de recuperações mássicas e metalúrgicas foram respectivamente: amostra A (78,30% e 95,13%); amostra B (50,75% e 96,83%) e amostra C (68,59% e 84,08%). Como resultados do estudo, observa-se a obtenção de um concentrado comercializável para a amostra C, com teor de Fe superior a 62,50% e teor de SiO2 inferior a 8,5%. As amostras A e B não alcançaram o padrão comercial, entretanto, uma blendagem com um material mais rico poderia ser uma opção para correção dos teores.

 

The Arcelor Mittal Mining Serra Azul unit generates a tailings from the jigging process during sinter feed iron ore concentration. This material is stacked and not marketed due to characteristics that do not conform to the quality standards defined by the steel market. The present study proposes the technological characterization of this tailing, through the techniques of granulometric classification, X-ray fluorescence, X-ray diffraction and optical microscopy. Subsequently, the route of magnetic concentration of high intensity in rougher stage is proposed for three different granulometric bands. Sample A- (-5.00mm + 2.36mm), Sample B- (-2.36mm + 0.60mm) and Sample C- (-0.60mm). After the concentration tests, the values of mass and metallurgical recoveries were respectively: sample A (78.30% and 95.13%); sample B (50.75% and 96.83%) and sample C (68.59% and 84.08%). As results of the study, it is possible to obtain a commercially available concentrate for sample C, with a Fe content of more than 62,50% and a SiO2 content of less than 8.5%. Samples A and B did not reach the commercial standard, however, blending with a richer material could be an option to correct the contents.

Palavras-chave

Minério de ferro; Rejeito; Caracterização; Concentração.

Iron ore; Waste; Description; Concentration

Como citar

Barbosa, Osmar Henrique Costa; Prado, Ivon Luis Silva; Barbosa, Ludmila Samara; Fernandes, Manoel Robério Ferreira. CARACTERIZAÇÃO TECNOLÓGICA E TRATAMENTO DE UM REJEITO GROSSO DE MINÉRIO DE FERRO POR CONCENTRAÇÃO MAGNÉTICA DE ALTA INTENSIDADE , p. 155-167. In: 19° Simpósio de Mineração, São Paulo, 2018.