Título

EFEITO DA REVERSÃO DA MARTENSITA INDUZIDA POR DEFORMAÇÃO EM BAIXAS TEMPERATURAS SOBRE O COMPORTAMENTO ELETROQUÍMICO DO AÇO INOXIDÁVEL LEAN DUPLEX 2304

EFFECT OF STRAIN-INDUCED MARTENSITE REVERSE TRANSFORMATION IN LOW TEMPERATURESON THE ELECTROCHEMICAL BEHAVIOR OF LEAN DUPLEX 2304 STAINLESS STEEL

DOI

10.5151/2594-4711-39627

Downloads

Baixar Artigo 15 Downloads

Resumo

Aços inoxidáveis lean duplex (AILD) são um novo subgrupo de aços inoxidáveis duplex (AID) e foram desenvolvidos para serem alternativas econômicas em relação a aços bem estabelecidos no mercado, como o AID 2205. Durante operações de deformação severa, a austenita metaestável é parcialmente transformada em martensita. Após recozimento, essa transformação é revertida. O objetivo do trabalho foi avaliar o efeito da formação da martensita induzida e posterior recozimento em baixas temperaturas no comportamento eletroquímico do AILD 2304. Para isso, o AILD laminado a quente e recozido foi laminado a frio com uma redução de 74% da espessura. Posteriormente, fez-se um recozimento isotérmico entre temperaturas 500°C e 600° C por 0,5 h. Foram realizadas análises microestruturais, eletroquímica e ensaios de dureza Vickers. Os resultados indicaram que a laminação a frio levou à formação da martensita induzida por deformação e sua reversão se inicia em temperaturas entre 500°C e 550°C. Notou-se endurecimento das amostras recozidas a 400°C e 500°C quando comparado à amostra laminada a frio. A resistência à corrosão não foi prejudicada pela formação da martensita, porém sua reversão em temperaturas acima de 500°C levou a grande diminuição no potencial de pite e aumento do grau de sensitização do material.

 

Lean duplex stainless steels (LDSS) are a new subgroup of duplex stainless steels (DSS) and were developed to be cost-effective alternatives to well-established steels such as DSS 2205. During severe deformation operations, the metastable austenite is partially transformed into martensite. After annealing, this transformation is reversed. This work aims to evaluate the effect of the formation of induced martensite and subsequent annealing at lowtemperatures on the mechanical and electrochemical behavior of LDSS 2304. For this, the hot-rolled and annealed LDSS was cold-rolled with a 74% reduction in thickness. Subsequently, isothermal annealing was carried out between 400°C and 600°C for 0.5 h. Microstructural, electrochemical and Vickers hardness analyses was carried out. The results indicated that cold rolling led to the formation of martensite induced by deformation and its reversion starts at temperatures between 500°C and 550°C. Hardening of the annealed specimens at 400°C and 500°C was noted when compared to the cold-rolled sample. Corrosion resistance was not impaired by martensite formation, but its reversion at temperatures higher than 500°C led to a large decrease in the pitting potential and an increase in the degree of sensitization.

Palavras-chave

Aço inoxidável duplex; martensita induzida por deformação; reversão da martensita induzida por defor

Duplex stainless steel; strain-induced martensite; strain-induced martensite reversion; corrosion re

Como citar

Campideli, Victor Cardoso; Assumpção, Raphael França; Santos, Dagoberto Brandão; Sicupira, Dalila Chaves. EFEITO DA REVERSÃO DA MARTENSITA INDUZIDA POR DEFORMAÇÃO EM BAIXAS TEMPERATURAS SOBRE O COMPORTAMENTO ELETROQUÍMICO DO AÇO INOXIDÁVEL LEAN DUPLEX 2304 , p. 54-66. In: 21° Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas (ENEMET), São Paulo, 2023.