A LIGA ZAMAC é UMA LIGA NãO-FERROSA COMPOSTA POR: ZINCO (ZN), ALUMíNIO (AL), COBRE (CU) E MAGNéSIO (MG). ELA é UTILIZADA PRINCIPALMENTE NO SETOR AUTOMOBILíSTICO PARA A PRODUçãO DE PEçAS COM FORMATOS COMPLEXOS DEVIDO A SUAS BOAS PROPRIEDADES MECâNICAS, PODE SER UTILIZADO COMO PROTEçãO CATóDICA PARA CASCOS DE NAVIOS E TUBULAçõES POIS POSSUI ALTA RESISTêNCIA à CORROSãO, E é UMA ALTERNATIVA DE SUBSTITUIçãO AO LATãO POR POSSUIR DESEMPENHO MECâNICO PARECIDO. ESTE TRABALHO APRESENTA ANáLISES QUANTO àS PROPRIEDADES MECâNICAS E CORROSIVAS DA LIGA ZAMAC-5, ATRAVéS DA ANáLISE QUíMICA FEITA POR ESPECTROMETRIA DE EMISSãO óTICA A FIM DE COMPARAR COM A NORMA ASTM B 240-22, QUE APRESENTOU COMPATIBILIDADE EM COMPARAçãO à LIGA UTILIZADA. A CORROSãO ESTá SENDO ANALISADA ATRAVéS DOS ENSAIOS SUBMERSOS EM SOLUçãO SALINA, COM ADIçãO DE CHIPS PARA AUMENTAR OU DIMINUIR O ESPAçO INTERATôMICO ENTRE AS MOLéCULAS DE ZINCO, E SERãO SUBMETIDAS AO ENSAIO DE POLARIZAçãO POTENCIODINâMICA. Já AS PROPRIEDADES QUANTO A RESISTêNCIA à TRAçãO E DUREZA, SERãO ANALISADOS ATRAVéS DE ENSAIOS. OS RESULTADOS ESPERADOS SãO QUE A LIGA NãO POSSUA UM GRANDE MóDULO DE ELASTICIDADE POR SER UMA PEçA FUNDIDA, CUJO PODE HAVER IRREGULARIDADES EM SUA MICROESTRUTURA QUE RESULTARãO EM DIFERENTES RESULTADOS AO LONGO DOS ENSAIOS.
THE ZAMAK ALLOY IS A NON-FERROUS ALLOY THAT IS PRODUCED FOR THE UNION OF FOUR ELEMENTS: ZINC (ZN), ALUMINUM (AL), MAGNESIUM (MG) AND COOPER (CU). THIS ALLOY IS USED IN THE AUTOMOBILE INDUSTRY TO PRODUCE PARTS WITH COMPLEXES GEOMETRIES DUE TO YOUR GOOD MECHANICAL PROPERTIES, CAN BE USED AS CATHODIC PROTECTION FOR HULL OF A BOAT AND PIPES BECAUSE IT HAS HIGH CORROSION RESISTANCE, AND IS AN ALTERNATIVE WAY TO REPLACE BRASS FOR OWNING MECHANICAL PERFORMANCE SIMILAR. THIS STUDY PRESENTS ANALYSIS AND INVESTIGATIONS ABOUT THE MECHANICAL AND CORROSIVE PROPERTIES OF ZAMAK-5 ALLOY, BY CHEMICAL ANALYSIS MADE BY OPTICAL EMISSION SPECTROMETRY TO COMPARE WITH THE STANDARD ASTM B 240-22, THAT SHOWS COMPATIBILITY WITH THE ALLOY USED. THE CORROSION IS BEING ANALYZED THROUGH TESTS SUBMERGED IN SALINE SOLUTION, WITH ADDITION OF CHIPS TO INCREASE OR DECREASE THE INTERATOMIC SPACE BETWEEN THE ZINC MOLECULES, WILL BE SUBJECTED TO THE POTENTIODYNAMIC POLARIZATION TEST. THE PROPERTIES OF TENSILE STRENGTH AND TOUGHNESS WILL BE ANALYZED THROUGH TESTS. THE EXPECTED RESULTS ARE THAT THE ALLOY DOES NOT HAVE A LARGE MODULUS OF ELASTICITY AS IT IS A CAST PIECE, WHICH MAY CAUSE IRREGULARITIES IN ITS MICROSTRUCTURE THAT WILL RESULT IN DIFFERENT RESULTS THROUGHOUT THE TESTS.
Palavras-chave
Zamac-5; Proteção Catódica; Ligas de zinco; Propriedades Mecânicas.
Zamak-5; Cathodic Protection; Zinc Alloys; Mechanical Properties.
Como citar
SANTOS, CLARA DA SILVA;
SOARES, FELIPE RAMON CIRINO;
SANTOS, CARLA ISABEL DOS.
ESTUDO DAS PROPRIEDADES DE CORROSÃO E DO COMPORTAMENTO MECÂNICO DA LIGA ZAMAC-5
,
p. 601-607.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-41368