ESTUDO DAS VARIÁVEIS DE COALESCIMENTO DE NÓDULOS DE FERRO-CARBONO A PARTIR DE MISTURAS E PELOTAS AUTORREDUTORAS NO FORNO ROTATIVO A 1.673 E 1.773 K: STUDY OF COALESCING VARIABLES OF IRON-CARBON NUGGETS FROM MIXTURES AND SELF-REDUCING PELLETS IN THE ROTARY KILN AT 1673 AND 1773 K

Nogueira, Alberto Eloy Anduze; Zambrano, Adolfo Pillihuaman; Takano, Cyro; Mourão, Marcelo Breda; Neira, John Bernardo Vilca; ,

doi:10.5151/2594-357X-17494

Anais dos Seminários de Redução, Minério de Ferro e Aglomeração

ISSN 2594-357X

40º Seminário de Redução de Minério de Ferro e Matérias-Primas e 11º Simpósio Brasileiro de Minério de Ferro — vol. 40, num.40 (2010)

Título

ESTUDO DAS VARIÁVEIS DE COALESCIMENTO DE NÓDULOS DE FERRO-CARBONO A PARTIR DE MISTURAS E PELOTAS AUTORREDUTORAS NO FORNO ROTATIVO A 1.673 E 1.773 K

STUDY OF COALESCING VARIABLES OF IRON-CARBON NUGGETS FROM MIXTURES AND SELF-REDUCING PELLETS IN THE ROTARY KILN AT 1673 AND 1773 K

Autoria

Nogueira, Alberto Eloy Anduze; Zambrano, Adolfo Pillihuaman; Takano, Cyro; Mourão, Marcelo Breda; Neira, John Bernardo Vilca; ,

10.5151/2594-357X-17494

Downloads

Baixar Artigo 67 Downloads

Resumo

Uma das possibilidades tecnológicas obtidas com a redução de minério de ferro por autorredução é a obtenção de nódulos de ferro-carbono diretamente no processo, como no processo ITmk3. Para compreender melhor o processo de obtenção de nódulos de ferro-carbono no forno rotativo a 1673 e 1773 K, a partir de misturas e pelotas autorredutoras, foi estudado o efeito das seguintes variáveis: temperatura de processamento, temperatura liquidus da escória, quantidade de redutor, e tipo de conformação. Foi empregada uma adaptação do teste de desagregação por tambor (ASTM E279-97) e validado por moagem manual, para medir o grau de coalescimento dos nódulos de ferro-carbono. Como resultados obtiveram-se: O incremento da temperatura de processamento aumenta o processo de coalescimento. A elevada temperatura liquidus da escória, obstaculiza o processo de coalescimento. O incremento da quantidade de redutor acima das necessidades de redução e carburação, restringem o processo de coalescimento. As misturas autorredutoras apresentam um maior grau de coalescimento do que as pelotas autorredutoras

One of the technological possibilities obtained by the reduction of iron ore by self-reduction is to obtain iron-carbon nuggets directly in the process, as in ITmk3 process.To better understand the process of obtain iron-carbon nuggets in a rotary kiln at 1673 and 1773 K from mixtures and self reducing pellets was studied the effect of following parameters: processing temperature, the slag liquidus temperature, the amount of reducer, and the type of conformation. Was used an adaption of the drum test (ASTM E279-97) and validated by manual grinding to measure the degree of coalescence of iron-carbon nuggets. As results were obtained: The increase in processing temperature increases the coalescence process. The high liquidus temperature of the slag, hinder the coalescing process. Increasing the amount of reducer above the needs for reduction and carburization, restrict the coalescence process. Self-reducing mixtures show better degree of coalescence than that of self-reducing pellets.

Palavras-chave

Pelotas autorredutoras; Misturas; Escória; Coalescimento; Nódulos.

Self-reducing pellets; Mixtures; Slag; Coalescence; Nuggets.

Como citar

Nogueira, Alberto Eloy Anduze; Zambrano, Adolfo Pillihuaman; Takano, Cyro; Mourão, Marcelo Breda; Neira, John Bernardo Vilca; ,. ESTUDO DAS VARIÁVEIS DE COALESCIMENTO DE NÓDULOS DE FERRO-CARBONO A PARTIR DE MISTURAS E PELOTAS AUTORREDUTORAS NO FORNO ROTATIVO A 1.673 E 1.773 K , p. 481-492. In: 40º Seminário de Redução de Minério de Ferro e Matérias-Primas e 11º Simpósio Brasileiro de Minério de Ferro, Belo Horizonte, 2010.