ESTUDO DO COMPORTAMENTO MECÂNICO EM COMPRESSÃO DE MATERIAL CIMENTÍCIO SUBMETIDO A VARIAÇÃO TÉRMICA

STUDY OF THE MECHANICAL BEHAVIOR IN COMPRESSION OF CEMENTILE MATERIAL SUBJECTED TO THERMAL VARIATION

DOI

10.5151/2594-4711-41015

Downloads

Baixar Artigo 1 Downloads

Resumo

A ARGAMASSA é UM COMPONENTE FUNDAMENTAL NA CONSTRUçãO CIVIL, UTILIZADA EM ASSENTAçãO DE PISOS, TIJOLOS E OUTRAS FUNçõES COMO IPERMEABILIZAR E ETC. QUANDO EXPOSTA A ALTAS TEMPERATURAS, A RESISTêNCIA DA ARGAMASSA DIMINUI CONSIDERAVELMENTE, ALTERANDO SUAS DEVIDAS PROPRIEDADES. O PRESENTE TRABALHO, EXPLORA O COMPORTAMENTO DE MATERIAIS CIMENTíCIOS SOB VARIAçõES TéRMICAS, FOCANDO NA ANáLISE DA RETRAçãO VOLUMéTRICA, DEFORMAçãO E RESISTêNCIA à COMPRESSãO. OS CORPOS DE PROVA DE ARGAMASSA FORAM PREPARADOS COM CIMENTO PORTLAND CP II, AREIA NATURAL E áGUA, E APóS 28 DIAS DE CURA, FORAM EXPOSTOS A TEMPERATURAS DE 25°C, 250°C E 350°C POR 60 MINUTOS, SEGUIDO POR ENSAIOS DE COMPRESSãO. OS RESULTADOS INDICARAM UMA REDUçãO SIGNIFICATIVA NA RESISTêNCIA à COMPRESSãO E UM AUMENTO NA RETRAçãO VOLUMéTRICA COM O AUMENTO DA TEMPERATURA. CONCLUI-SE QUE AS VARIAçõES TéRMICAS IMPACTAM NEGATIVAMENTE A DURABILIDADE DAS ESTRUTURAS DE ARGAMASSA, E ESTRATéGIAS DE ALíVIO, COMO A ADIçãO DE ADITIVOS POZOLâNICOS, SãO NECESSáRIAS PARA MELHORAR A RESISTêNCIA TéRMICA E GARANTIR A SEGURANçA E DURABILIDADE DAS CONSTRUçõES.

 

MORTAR IS A FUNDAMENTAL COMPONENT IN CIVIL CONSTRUCTION, USED TO LAY FLOORS, BRICKS AND OTHER FUNCTIONS SUCH AS WATERPROOFING, ETC. WHEN EXPOSED TO HIGH TEMPERATURES, THE RESISTANCE OF THE MORTAR DECREASES CONSIDERABLY, ALTERING ITS PROPERTIES. THE PRESENT WORK EXPLORES THE BEHAVIOR OF CEMENTITIOUS MATERIALS UNDER THERMAL VARIATIONS, FOCUSING ON THE ANALYSIS OF VOLUMETRIC SHRINKAGE, DEFORMATION, AND COMPRESSIVE STRENGTH. THE MORTAR SPECIMENS WERE PREPARED WITH PORTLAND CP II CEMENT, NATURAL SAND, AND WATER, AND AFTER 28 DAYS OF CURING, THEY WERE EXPOSED TO TEMPERATURES OF 25°C, 250°C AND 350°C FOR 60 MINUTES, FOLLOWED BY TEMPERATURE TESTS. COMPRESSION. THE RESULTS INDICATED A SIGNIFICANT REDUCTION IN COMPRESSIVE STRENGTH AND AN INCREASE IN VOLUMETRIC SHRINKAGE WITH INCREASING TEMPERATURE. IT IS CONCLUDED THAT THERMAL VARIATIONS NEGATIVELY IMPACT THE DURABILITY OF MORTAR STRUCTURES, AND RELIEF STRATEGIES, SUCH AS THE ADDITION OF POZZOLANIC ADDITIVES, ARE NECESSARY TO IMPROVE THERMAL RESISTANCE AND ENSURE THE SAFETY AND DURABILITY OF CONSTRUCTIONS.

Palavras-chave

Argamassa; Altas temperaturas; Portland; Compressão.

Mortar; High temperatures; Portland; Compression.

Como citar

SOUSA, PALOMA SUELLEN LIMA DE; SOUZA, SARAH GABRIELLY BRANDÃO DE; NASCIMENTO, JOELLY VERA; NASCIMENTO, DAMARES DA CRUZ BARBOSA; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERONICA SCARPINI. ESTUDO DO COMPORTAMENTO MECÂNICO EM COMPRESSÃO DE MATERIAL CIMENTÍCIO SUBMETIDO A VARIAÇÃO TÉRMICA , p. 328-335. In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo, Brasil, 2024.