ESTUDO SOBRE CARACTERIZAÇÃO E ROTAS DE LIXIVIAÇÃO PARA ESCÓRIA DE REDUÇÃO FERRO/NÍQUEL

STUDY ON CHARACTERIZATION AND LEACHING ROUTES FOR IRON/NICKEL REDUCTION SLAG

Autoria

SANTO, YARA BEATRIZ RODRIGUES DO ESPIRITO

SANTO, YARA BEATRIZ RODRIGUES DO ESPIRITO

Eu sou esse autor

DOI

10.5151/2594-357X-40574

Downloads

Resumo

O SETOR MINERO-METALúRGICO é ESSENCIAL PARA A ECONOMIA, IMPULSIONANDO O AVANçO TECNOLóGICO E CIENTíFICO, EMBORA TRAGA IMPACTOS AMBIENTAIS NEGATIVOS DEVIDO AOS RESíDUOS GERADOS. ESTE ESTUDO PROPõE UMA POSSíVEL ROTA DE RECICLAGEM PARA RESíDUOS DE MINERAçãO AO FOCAR NA RECUPERAçãO DE METAIS ATRAVéS DA LIXIVIAçãO E CLASSIFICAR AS ESCóRIAS RESULTANTES DA REDUçãO DE FERRO/NíQUEL (FENI), A PARTIR DE NORMAS TéCNICAS. ATRAVéS DISSO A RECUPERAçãO DE RESíDUOS METáLICOS VISA A DESTINAçãO SUSTENTáVEL DAS ESCóRIAS. A AMOSTRA FOI COMINUíDA PARA GRANULOMETRIA DE 0,3MM. A SOLUçãO DE NAOH 1N FOI INDICADA COMO LIXIVIANTE PARA 100G DO MATERIAL. FORAM USADOS O AGITADOR TIPO WAGNER (18H, 30 RPM) E O SISTEMA DE FILTRAçãO A VáCUO PARA A COLETA APóS O ENSAIO. OS MATERIAIS RETIDOS SECOS, SOLUçõES FILTRADAS E LAVADAS FORAM ANALISADAS POR DRX, FRX E ICP, REVELANDO A PRESENçA DE FORSTERITA, MINERAL DE SILICATOS DE MAGNéSIO E FERRO, E TEORES ELEMENTARES DE SI, MG, FE E NI DE 19%, 18%, 15% E 0,14% RESPECTIVAMENTE. COM RELAçãO AO PARâMETRO DE CROMO TOTAL, FOI ENCONTRADO UM VALOR ACIMA DE 5MG/L ESTABELECIDO PELA NORMA NBR 10004. OS TEORES DE AL, FE E MN TAMBéM FICARAM ACIMA DO PADRãO PERMITIDO

THE MINING SECTOR IS ESSENTIAL TO THE ECONOMY, DRIVING TECHNOLOGICAL AND SCIENTIFIC PROGRESS, ALTHOUGH IT HAS NEGATIVE ENVIRONMENTAL IMPACTS DUE TO THE WASTE GENERATED. THIS STUDY PROPOSES A POSSIBLE RECYCLING ROUTE FOR MINING WASTE, FOCUSING ON THE RECOVERY OF METALS AFTER COMPARATIVE LEACHING WITH TECHNICAL STANDARDS, WITH THE AIM OF CLASSIFYING THE SLAG RESULTING FROM THE REDUCTION OF IRON/NICKEL (FENI) AND ACHIEVING THE RECOVERY OF METALLIC WASTE, CONTRIBUTING TO THE SUSTAINABLE DISPOSAL OF MINING WASTE. THE SAMPLE WAS COMMINUTED TO A PARTICLE SIZE OF 0.3MM. A 1N NAOH SOLUTION WAS USED AS A LEACHING AGENT FOR 100G OF THE MATERIAL. A WAGNER SHAKER (18H, 30 RPM) AND A VACUUM FILTRATION SYSTEM WERE USED FOR COLLECTION AFTER THE TEST. THE DRY RETAINED MATERIALS, FILTERED AND WASHED SOLUTIONS WERE ANALYZED BY XRD, XRF AND ICP, REVEALING THE PRESENCE OF FORSTERITE, A MINERAL OF MAGNESIUM AND IRON SILICATES, AND ELEMENTAL CONTENTS OF SI, MG, FE AND NI OF 19%, 18%, 15% AND 0.14% RESPECTIVELY. WITH REGARD TO THE TOTAL CHROMIUM PARAMETER, A VALUE ABOVE 5MG/L ESTABLISHED BY THE NBR 10004 STANDARD WAS FOUND. THE LEVELS OF AL, FE AND MN WERE ALSO ABOVE THE PERMITTED STANDARD

Palavras-chave

Hidrometalurgia; Lixiviação; Escória; Sustentabilidade

Hydrometallurgy; Leaching; Slag; Sustainability.