INFLUÊNCIA DA TEMPERATURA DE PRÉ-AQUECIMENTO NA RESISTÊNCIA MECÂNICA DE JUNTAS SOLDADAS DE UM AÇO DE ULTRA-ALTA RESISTÊNCIA

INFLUENCE OF THE PREHEATING TEMPERATURE ON THE MECHANICAL STRENGTH OF WELDED JOINTS MADE OF AN ULTRAHIGH-STRENGTH STEEL

Autoria

Filho, José Roque; Neto, Carlos de Moura; Garcia, José Augusto Orlowski de; Guimarães, Valdir Alves

DOI

10.5151/2594-5327-0431

Downloads

Baixar Artigo 50 Downloads

Resumo

Neste trabalho é verificada a influência da temperatura de pré-aquecimento na resistência mecânica de juntas soldadas em chapa de pequena espessura de um aço de ultra-alta resistência de médio-carbono e baixa liga. A soldagem foi realizada em passe único pelo processo Plasma Arc Welding (PAW), com a técnica keyhole, nas condições sem pré-aquecimento e com pré-aquecimento de 100°C. A caracterização do material foi feita em duas condições: “como soldado” e “tratado termicamente”. Os corpos-de-prova (cdps) de tração foram submetidos a ciclos térmicos de normalização, têmpera e duplo revenimento e suas fraturas foram caracterizadas por MEV. Observa-se que as juntas soldadas com pré-aquecimento apresentam resistência máxima à tração 1,8% menor que as juntas soldadas à temperatura ambiente, apesar de não ter sido constatada diferença de tamanho de grão entre as amostras representativas das duas condições de soldagem.

 

The objective of this study is to verify the influence of the preheating temperature on the mechanical strength of welded joints on a thin sheet made of a medium-carbon low-alloy ultrahigh-strength steel. The welding was done by Plasma Arc Welding Process (PAW) using the keyhole technique, single pass. The weldings were performed at room temperature and at a preheating temperature of 100°C. The material characterization was obtained from the welded sheets in two conditions: as welded and in the heat-treated condition. The specimens for tension tests were heat- treated by normalizing, quenching and double tempering cycles and, after the tests, their fractures were inspected by SEM. It is observed that the preheating welded joints present maximum strength at a tension 1.8% lower than the strength presented by the joints welded at room temperature. However, no difference in grain size between the representative samples of the two welding conditions is observed.