PARÂMETROS TERMODINÂMICOS E CINÉTICOS DA DESSULFURAÇÃO ATRAVÉS DE RESÍDUO DE MÁRMORE

DESULPHURIZATION PHYSICAL CHEMISTRY BY MARBLE WASTE

DOI

10.5151/2594-5300-20833

Downloads

Baixar Artigo 94 Downloads

Resumo

Este trabalho apresenta uma análise cinética e termodinâmica da utilização de misturas à base de resíduo de mármore na dessulfuração de ferro-gusa. Para a realização da dessulfuração foram utilizados: cal, resíduo de mármore, fluorita, e ferro-gusa. Diferentes misturas destes materiais foram adicionadas em um banho de ferro-gusa a 1.450°C. Amostras do metal foram retiradas através de amostradores a vácuo nos tempos de 5 minutos, 10 minutos, 15 minutos, 20 minutos e 30 minutos e feitas suas análises para checar a variação de enxofre. Com base nos resultados das análises químicas do metal e da mistura dessulfurante utilizadas, foram calculadas a capacidade de sulfeto das misturas, o coeficiente de partição de enxofre e os valores do coeficiente de transporte de massa do enxofre. Os resultados obtidos mostraram a viabilidade técnica da utilização do resíduo como agente dessulfurante.

 

The objective of this paper is to present kinetics and thermodynamic analysis of desulphurization process in a hot metal pre-treatment with marble waste mixtures. It was used in this study: marble waste, fluorspar, ash, lime, and hot metal. Four mixtures were made and added to a liquid hot metal – with known chemical composition – at temperature of 1.450°C. Mass of each element was calculated from its chemical analysis and comparison with an industrial mixture. All four mixtures were used in experiments stirred by mechanical stirrer. Samples were collected by vacuum sampling at the time of 5 minutes, 10 minutes, 15 minutes, 20 minutes, and 30 minutes, and made analysis to check sulfur variation in the bath. The results were kinetics and thermodynamic analyzed and it was verified the possible utilization of marble waste like desulfurizer.

Palavras-chave

Resíduo de mármore; Florita; Dessulfuração de ferro-gusa.

Marble waste; Fluospar; Hot metal desulphurization.