Os instrumentos endodônticos rotatórios proporcionaram importantes avanços na terapia endodôntica, reduzindo alterações morfológicas nos canais radiculares e propiciando uma preparação mais eficiente. Esses instrumentos são confeccionados utilizando ligas superelásticas de NiTi na forma de fios trefilados e recozidos. Neste trabalho, foram caracterizados três fios de NiTi de 1,0 mm de diâmetro, utilizados na confecção de diferentes instrumentos endodônticos rotatórios. De acordo com os fabricantes, dois fios foram processados de maneira convencional por trefilação e tratamento térmico a baixa temperatura, enquanto que o terceiro foi submetido a um tratamento térmico adicional. A composição química dos fios foi analisada por espectroscopia de energia de raios X, as fases presentes foram identificadas por difratometria de raios X e as temperaturas de transformação foram determinadas por calorimetria exploratória diferencial. As propriedades mecânicas foram avaliadas em ensaios de tração e por microdureza Vickers. As propriedades encontradas nos três fios foram avaliadas em relação à aplicação pretendida. Verificou-se que o tratamento térmico adicional produziu essencialmente aumento nas temperaturas e diminuição na tensão de transformação dos fios.
The rotary endodontic instruments provided important advances in the endodontic therapy, reducing morphological changes in root canals and providing a more efficient preparation. These instruments are made using superelastic NiTi alloys in the form of cold drawn and annealed wires. In this study, three NiTi wires with 1.0 mm in diameter used in the manufacture of different rotary endodontic instruments were characterized. According to the manufactures, two wires were processed in a conventional manner by cold drawing and annealing at low temperature, while the third was submitted to an additional heat-treatment. The chemical composition of the wires was analyzed by X-ray energy dispersive spectroscopy, the phases present were identified by X-ray diffraction and the transformation temperatures were determined by differential scanning calorimetry. The mechanical properties were evaluated in tensile tests and microhardness measurements. The properties found in the three wires were analyzed in relation to the intended application. It has been verified that the additional heat treatment produced essentially an increase in the transformation temperatures and a decrease in the transformation stress.
Palavras-chave
Ligas NiTi; Superelasticidade; Instrumentos endodônticos.
NiTi alloys; Superelasticity; Endodontic instruments.
Como citar
Oliveira, Isabela Ibrahim;
Araújo, Letícia Mangualde;
Pereira, Érika Sales Joviano;
Bahia, Maria Guiomar de Azevedo;
Buono, Vicente Tadeu Lopes.
PROPRIEDADES FÍSICAS E MECÂNICAS DE TRÊS FIOS DE NiTi UTILIZADOS NA CONFECÇÃO DE INSTRUMENTOS ENDODÔNTICOS
,
p. 1279-1287.
In: 66º Congresso Anual da ABM,
São Paulo,
2011.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-17899