A FORMAÇÃO DA ESTRUTURA DO METAL DURO (WC/6%Co) EM CONDIÇÕES DE ALTAS PRESSÕES E ALTAS TEMPERATURAS

THE FORMATION OF HARD METAL (WC/6%Co) STRUCTURE AT HIGH PRESSURE AND HIGH TEMPERATURE CONDITIONS

Authorship

Gomes, Cristiane Maria Fernandes; Brobovnitchii, Guerold Sergueevitch; Filgueira, Marcello; Holanda, José Nilson França de

Gomes, Cristiane Maria Fernandes

I am this author

Brobovnitchii, Guerold Sergueevitch

I am this author

Filgueira, Marcello

I am this author

Holanda, José Nilson França de

I am this author

DOI

10.5151/2594-5327-0128

Downloads

Abstract

A indústria mundial de ferramentas de corte está a cada dia buscando métodos de melhoria das propriedades de metal duro para satisfazer a crescente demanda dos consumidores. Um dos métodos visados é a aplicação de alta pressão (acima de 3,0 GPa) na sinterização de compactos de metal duro. No presente trabalho foi feito um estudo preliminar da possibilidade de formação de pastilhas de metal duro com composição WC/6%Co em condições de altas pressões (3,0 a 7,0 GPa) e temperaturas de 1200, 1300 e 1400oC. Os resultados mais efetivos foram obtidos sob a temperatura de 1200oC. Além disso, os resultados mostraram que as amostras submetidas a altas pressões apresentaram estrutura fina, dureza e microdureza aumentadas e grau de desgaste mais alto comparados com àquelas obtidas pelo método convencional.

The world industry of cutting tools is each day finding improvement methods of hard metal properties to satisfy the increasing demand of the consumers. One of sighted methods is the application of high pressure (up 3,0 GPa) on sintering of hard metal compacts. In the present work, it was done a preliminary study of the possibility of formation of hard metal pastilles with WC/6%Co composition at high pressure (3,0 up to 7,0 GPa) and temperatures of 1200, 1300 e 1400oC conditions. The results more effective were obtained under temperature of 1200oC. In addition, the results showed that the submitted to high pressures samples presented fine structure, increased hardness and microhardness and more high degree of wear compared with that obtained by convencional methods.