Title

A INFLUÊNCIA DA VARIAÇÃO DO TEOR DE SILÍCIO NA LIGA DA SÉRIE 60001

THE INFLUENCE OF THE SILICON CONTENT VARIATION IN 6000 SÉRIES ALLOY

Authorship

Moreira, Darci Augusto; Maia, Raimunda Figueiredo da Silva; Moreira, Aline Emanuelle Albuquerque; Maneschy, Carlos Edílson de Almeida; Quaresma, José Maria do Vale

Moreira, Darci Augusto

I am this author

Maia, Raimunda Figueiredo da Silva

I am this author

Moreira, Aline Emanuelle Albuquerque

I am this author

Maneschy, Carlos Edílson de Almeida

I am this author

Quaresma, José Maria do Vale

I am this author

DOI

10.5151/2594-5327-0122

Downloads

Abstract

O objetivo deste trabalho é desenvolver uma análise sobre o comportamento do silício nas ligas da série 6000, em particular as ligas 6101 e 6201 utilizadas para transmissão de energia elétrica. Para esse fim, utilizou-se da fundição direta em condições transitórias de calor, fazendo-se uso de um dispositivo em forma de “U” e ligas Al-0.6% Mg - (0.4; 0.8; 1.2) % Si. Os dados experimentais foram coletados do ensaio de tração e o aspecto fratográfico foi utilizado para confirmação dos resultados do ensaio de tração. Esses dados apontaram para o decréscimo das propriedades mecânicas (tração e alongamento) na proporção em que o teor de silício é acrescido na liga. Conclui-se que é ineficaz adicionar silício acima dos limites das ligas, na busca do equilíbrio entre excelentes propriedades mecânicas e elétricas, que possibilitem enquadrar a liga aos parâmetros exigidos para cabos condutores de transmissão elétrica.

The objective of this work is to develop analysis about the behavior of the silicon in the series 6000 alloy, in matter the 6101 and 6201 alloys used for electric power transmission. For this, was used of the direct foundry in transitory conditions of heat, being made use of a device in the shape of “U” and casting of Al-0.6%Mg – (0.4; 0.8; 1.2) % Si. The experimental dates were collected of strength tests and failure aspect was used for confirmation of the results of the strength tests. Those dates shows a decrease of the mechanical properties (strength and stretch) in the proportion in that the silicon content is added into alloy. It reason that is ineffective to add silicon above the limits of the series 6000 alloys, with the results also indicating that there are possibilities excellent mechanical properties, that it makes possible to frame the alloy to the parameters demanded for conductive cables of electric transmission.

Keywords

Condução elétrica; Ligas de alumínio e silício; Propriedades mecânicas.

Power transmission; Aluminum and silicon binary alloy; Mechanical properties.