Abstract

A distorção após tratamento térmico a vácuo foi investigada para três aços ferramentas para trabalho a frio: o tradicional aço AISI D2 (~1.5%C 12%Cr 1% Mo) ; um aço recentemente desenvolvido (~1%C 8% Cr 2% Mo 1% V) ; um aço produzido por metalurgia do pó (P/M), (~ 0.8% ̈ C 7.5%Cr 1.3%Mo 2.75% V) . A distorção foi avaliada através de medidas de não-circularidade com um máquina de coordenadas tri-dimensional. Os resultados mostraram que a forma e magnitude da distorção foi diferente para aço ao longo dos estágios de tempera e revenimento, e foi associada com a composição e microestrutura de cada aço. O tamanho, fração volumétrica e distribuição de carbonetos primários juntamente com o teor de austenita retida tiveram influência nas distorções abservadas. A menor distorção foi observada com o aço P/M, seguida pelo aço com 8%Cr e finalmente o aço AISI D2 que apresentou a maior distorção. A menor e mais uniforme distorção apresentada pelo aço P/M foi atribuida a presença de carbonetos primários mais esféricos, menores e mais uniformente distribuidos com comparado com os outros aços.

The distortion after vacuum heat treatment has been investigated for three cold work tool steels: a traditional 1.5% C 12%Cr 1% Mo 1%V, AISI D2 steel; a recently developed 1.0%C 8%Cr 2 %Mo 1.6%V steel and a 0.8%C 7.5%Cr 1.3%Mo 2.75%V (P/M) steel. The degree of distortion was assessed via out-of-roundness measurements, using a tri-dimensional measuring machine .The results showed that the shape and magnitude of distortion was different for each steel along the heat treatment stages and it is associated with the composition as well as the microstructural differences of each steel. The size, volume fraction and distribution of primary carbides, together the retained austenite content, all played important roles on the distortion after heat treatment under vacuum of the investigated steels. The smallest distortion were observed with P/M steel, followed closely by the 8%Cr steel and finally, by the conventional D2 steel. The smallest and more uniform distortion of the P/M steel has been attributed to its smaller, spherically shaped and better distributed primary carbides when compared with the both conventionally cast 8% or 12% Cr tool steels..

Keywords

Distorção: Metalurgia do pó; Aços ferramenta.

Distortion; P/M; Tool steels.