EFEITO DA RAZÃO PHR DA MATRIZ EPÓXI NAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS COM PARTÍCULAS DE DIAMANTE

THE EFFECT OF THE EPOXY MATRIX PHR RATIO ON THE MECHANICAL PROPERTIES OF DIAMOND PARTICLES DISPERESED COMPOSITES

Authorship

Monteiro, Sergio Neves; Menezes, Gustavo Wagner de; Skury, Ana Lúcia Diegues; Lopes, Felipe Perissé Duarte; Carvalho, Eduardo Atem de; D’Almeida, José Roberto Moraes

Monteiro, Sergio Neves

I am this author

Menezes, Gustavo Wagner de

I am this author

Skury, Ana Lúcia Diegues

I am this author

Lopes, Felipe Perissé Duarte

I am this author

Carvalho, Eduardo Atem de

I am this author

D’Almeida, José Roberto Moraes

I am this author

DOI

10.5151/2594-5327-0063

Downloads

Abstract

Estudou-se as propriedades mecânicas dos compósitos com partículas dispersas de diamante em matriz de resina epóxi curada com diferentes proporções de endurecedor caracterizadas pela razão phr. Estes compósitos foram previamente estudados para valores de phr correspondentes à relação estequiométrica e máxima resistência. No presente trabalho foi feita uma completa avaliação das propriedades mecânicas no amplo intervalo de phr de possível aplicação tecnológica. Foram fabricados compósitos com até 30% em peso de partículas de diamante dispersas em matriz epoxy do tipo DGEBA/TETA com diferentes phr variando de 7 a 21. Para todas as condições investigadas a resistência diminuiu com a quantidade incorporada de diamante. Para matrizes com phr acima do estequiométrico 13, os compósitos apresentaram melhor desempenho mecânico.

The mechanical properties of composites with dispersed diamond particles in epoxy matrix cured with different proportions of hardener to monomer ratio, characterized by the phr, were studied. These composites have been previously studied for phr values corresponding to the stoichiometric relation and the maximum strength. In the present work a complete evaluation of the mechanical properties was carried in a wide interval of phr with possible technological application. Composites with up to 30 wt. % of diamond particles dispersed in type DGEBA/TETA epoxy matrix were fabricated with phr ratios varying from 7 to 21. For all investigated conditions, the composite strength decreased with the amount of incorporated diamond. Matrices with phr above the stoichiometric 13 were associated with composites with better mechanical performance.