AVALIAÇÃO DA LIMPIDEZ DAS PLACAS DE AÇO ULTRA BAIXO CARBONO PROVENIENTES DO FLUXO INICIAL DO DISTRIBUIDOR DO LINGOTAMENTO CONTÍNUO

ULTRA LOW CARBON STEEL CLEANLINESS EVALUATION SLABS FROM CONTINUOUS CASTING INITIAL FLUX

DOI

10.5151/2594-5300-33556

Downloads

Baixar Artigo 131 Downloads

Resumo

O nível de inclusões presentes no aço líquido interfere diretamente na qualidade das placas produzidas por lingotamento contínuo e são determinantes na formação de defeitos superficiais em produtos laminados a frio. A reoxidação do aço, bem como a passagem de escória do distribuidor para o molde, a interação do aço com o pó de cobertura do distribuidor e com o pó fluxante, têm forte influência na limpidez das placas originadas no processo de solidificação no molde. No presente trabalho, avaliaram-se as inclusões formadas durante o início do processo de lingotamento contínuo para aços de ultra baixo teor de carbono, sob três diferentes condições de adição do pó de cobertura do distribuidor, além da própria condição padrão. O objetivo do estudo é reduzir a quantidade das inclusões e consequentemente, os defeitos superficiais em placas iniciais, por meio da relação com o teor de oxigênio no veio da máquina de lingotamento contínuo. Tal investigação visou fornecer informações para alterações nas condições do processo para melhoria da qualidade do produto final.

 

The inclusions level present in molten steel interferes directly in the slabs produced by continuous casting and are determinant in surface defects formation in cold rolled products. The steel reoxidation, as well as the slag carried from the tundish to the mold, the interaction of the steel with tundish covering powder and mold flux powder, have a strong influence on the slabs cleanliness originated in solidification process in the mold. In the present work, the inclusions formed during the beginning of the continuous casting process for ultra low carbon steels were evaluated, under three different conditions of addition from tundish powder covering, besides the standard condition itself. The study’s objective is to reduce the inclusions, and consequently, superficial defect in initial slabs and, it will be possible to identify them by means of the relation of the oxygen content in the continuous casting machine strand. Such research was intended to provide information for changes in the process conditions to improve the quality of the final product.

Palavras-chave

Distribuidor; Esfoliamento; Reoxidação; Inclusões

Tundish; Slivers; Reoxidation; Inclusions

Como citar

Moreira, Sérgio Roberto Lopes; Dias, Rodrigo Madrona; Martins, Rodrigo Seara; Oliveira, Leonardo José Silva de; Moreira, Fabiano Abrahão; Lemos, Leandro Rocha. AVALIAÇÃO DA LIMPIDEZ DAS PLACAS DE AÇO ULTRA BAIXO CARBONO PROVENIENTES DO FLUXO INICIAL DO DISTRIBUIDOR DO LINGOTAMENTO CONTÍNUO , p. 377-388. In: 50° Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, 2019.