Título

AVALIAÇÃO DAS PROPRIEDADES DE REDUÇÃO, AMOLECIMENTO E FUSÃO DE BRIQUETES DE CAREPA PARA USO EM ALTOS-FORNOS

EVALUATION OF THE REDUCTION, SOFTENING AND MELTING PROPERTIES OF MILL SCALE BRIQUETTES FOR BLAST FURNACES

Autoria

Assis, Otavio Henrique Matos de; Flores, Ismael Vemdrame; Alves, João Victor Souza; Bagatini, Maurício Covcevich

DOI

10.5151/2594-357X-34393

Downloads

Baixar Artigo 16 Downloads

Resumo

PARA A UTILIZAÇÃO DE RESÍDUOS SOB A FORMA DE AGLOMERADOS NOS REATORES SIDERÚRGICOS É NECESSÁRIO CONHECER SUAS PROPRIEDADES QUANDO SUBMETIDOS ÀS CONDIÇÕES REINANTES NO INTERIOR DOS MESMOS. A ZONA COESIVA É DE ESPECIAL INTERESSE NA OPERAÇÃO DE ALTOS FORNOS, POR INFLUENCIAR DIRETAMENTE NO FLUXO GASOSO EM SEU INTERIOR E, CONSEQUENTEMENTE NA SUA PRODUTIVIDADE. O PRESENTE TRABALHO TEVE COMO OBJETIVO DETERMINAR O COMPORTAMENTO DE AMOLECIMENTO E FUSÃO DE BRIQUETES PRODUZIDOS COM CAREPA, VISANDO SUA UTILIZAÇÃO EM ALTOS FORNOS. OS PRINCIPAIS PARÂMETROS OBTIDOS POR MEIO DESSES ENSAIOS FORAM AS TEMPERATURAS DE INÍCIO E FINAL DE ZONA COESIVA, MÁXIMA PERDA DE PRESSÃO NESSE INTERVALO E A INTEGRAL DA PERDA DE PRESSÃO NO INTERVALO DE ZONA COESIVA. ALÉM DISSO, FOI POSSÍVEL DESCREVER O COMPORTAMENTO DE REDUÇÃO DA AMOSTRA, SENDO ESTE DIVIDIDO EM TRÊS ESTÁGIOS: REDUÇÃO GÁS-SÓLIDO, RETARDO DE REDUÇÃO E REDUÇÃO NO ESTADO LÍQUIDO. DE MANEIRA GERAL, OS BRIQUETES TIVERAM UM DESEMPENHO PRÓXIMO AO APRESENTADO POR OUTRAS MATÉRIAS-PRIMAS JÁ CONSOLIDADAS E LARGAMENTE UTILIZADAS NA COMPOSIÇÃO DA CARGA FERROSA EM ALTOS-FORNOS

 

RECYCLING OF THE SOLID WASTE PRODUCED DURING IRON AND STEELMAKING PROCESSES PLAYS A KEY ROLE ON PROVIDING PROCESS SUSTAINABILITY FOR STEEL MILLS AROUND THE WORLD. FOR THOSE WASTES TO BE USED IN METALLURGICAL REACTORS IT IS CRITICAL TO UNDERSTAND THEIR BEHAVIOR WHILE UNDER THE CONDITIONS FOUND INSIDE THOSE REACTORS. THE COHESIVE ZONE IS OF SPECIAL INTEREST WHILE STUDYING OR RUNNING A BLAST FURNACE, SINCE IT CONTROLS GAS-FLOW DISTRIBUTION AND HENCE ITS PRODUCTIVITY. THUS, IN THIS STUDY, THE BEHAVIOR OF REDUCTION SOFTENING AND MELTING OF MILL SCALE BRIQUETTES WAS INVESTIGATED VIA SOFTENING AND MELTING EXPERIMENTS. THE MAJOR PARAMETERS OBTAINED WERE ITS COHESIVE ZONE STARTING AND ENDING TEMPERATURES, MAXIMUM PRESSURE DROP INSIDE THIS INTERVAL AND THE PRESSURE DROP INTEGRAL OVER THE COHESIVE ZONE INTERVAL. ALSO, THE SAMPLE’S REDUCTION BEHAVIOR WAS DESCRIBED THROUGH THREE STAGES: GAS-SOLID REACTION, REDUCTION RETARDATION AND MELT REDUCTION. ROUGHLY, THE BRIQUETTES SAMPLE’S HAD A SIMILAR PERFORMANCE OF THOSE MOST COMMONLY USED BLAST FURNACE BURDEN MATERIALS

Palavras-chave

Amolecimento e Fusão; Redução; Briquetes; Carepa.

Softening and Melting; Reduction; Briquettes; Mill Scale.