REDUÇÃO NA VARIAÇÃO DE NÍVEL DE AÇO NO MOLDE EM PLACAS DE AÇOS HSLA PERITÉTICOS PRODUZIDOS PARA A LAMINAÇÃO DE BOBINAS A QUENTE CONFORME NORMA ASTM A588-B: MOULD LEVEL FLUCTUATION REDUCTION ON PERICTETIC HSLA STEEL SLABS PRODUCED FOR THE HOT ROLLED COIL MILL ACCORDING TO ASTM A588-B STANDARDS

Incentivado pela diversificação dos produtos em aço, a demanda por graus cuja composição química esteja próxima da faixa peritética, tais como os aços HSLA (High Strength Low Alloy) e AHSS (Advanced High Strength Steel), tem aumentado. As crescentes exigências nas propriedades mecânicas e a redução de custo nas ligas são as razões para que esses aços sejam projetados próximos à faixa peritética, com o teor de carbono entre 0,09 e 0,16%. A produção de placas do aço ASTM A588-B, com o teor de carbono visado igual a 0,10%, apresentava expressiva variação do Nível de Aço no Molde (Ou Mould Level Fluctuation, MLF), aumentando a probabilidade de ocorrência de “Break-Out” (Rompimento de Pele) e a redução da qualidade de superfície das placas, com eventual ocorrência de Trincas Longitudinais. Outra limitação é a impossibilidade de troca de largura das placas, dependente da estabilidade do processo de Lingotamento Contínuo. Serão discutidas as ações tomadas visando a redução do MLF, baseada em alterações no Projeto de Liga, a comparação entre variáveis-chave do processo de Lingotamento Contínuo de Placas em dois cenários de Projeto de Liga além dos impactos em características de Propriedades Mecânicas do produto laminado, no caso bobinas processadas em Laminador Steckel.

Encouraged by the diversification of the steel products, the demand for the grades whose chemical composition is close to the Perictetic Region, as for example the HSLA (High Strength Low Alloy) and AHSS (Advanced High Strength Steel) Steels are growing. The always increasing demands on the Mechanical Properties and the reduction of alloying costs are the main reasons for the chemical composition to be near the Perictetic Region, with the Carbon content between 0,09% and 0,16%. The production of Continuously Cast Slabs, Steel Grade ASTM A588-B, with the Carbon content equal to 0,10%, shown expressive Mould Level Fluctuation, MLF, increasing the probability of occurrence of Break-Outs and the reduction of slab’s surface quality. Longitudinal Cracks can occur with this scenario. Another problem is the impossibility to change the width of the slabs, a process that is highly dependent on the process stability. This paper will discuss the actions performed with the objective to reduce the MLF based in some changing of the Alloy Design, the comparison between Slab Continuous Casting Key Process Variables in two different scenarios of Steel Grades and the impact on alloying cost and the Mechanical Properties of Hot Rolled Coils from a Steckel Mill.

Palavras-chave

Reação Peritética, Transformação Peritética, Lingotamento Contínuo de Placas, Variação de Nível de A

Perictetic Reaction, Perictetic Transformation, Slab Continuous Casting, Mould Level Fluctuation, Al

Como citar

Oliveira, Alisson Paulo de; Rossi, Edson Hugo; Cohn, Jorge Adam Cleto; Martins, Cleiton Arlindo; Carvalho, Carlos Vinícius Domingos de; Filho, Carlos José Carneiro. REDUÇÃO NA VARIAÇÃO DE NÍVEL DE AÇO NO MOLDE EM PLACAS DE AÇOS HSLA PERITÉTICOS PRODUZIDOS PARA A LAMINAÇÃO DE BOBINAS A QUENTE CONFORME NORMA ASTM A588-B , p. 332-343. In: 48º Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, 2017.
ISSN: 2594-5300 , DOI 10.5151/1982-9345-30358