DESENVOLVIMENTO DE AÇO ALTO CARBONO BAIXA LIGA (BW BL 50CRMO4) NA ARCELORMITTAL TUBARÃO E WAELZHOLZ BRASMETAL LAMINAÇÃO PARA APLICAÇÃO DIRETA EM SABRE DE MOTOSSERRA: DEVELOPMENT OF HIGH-CARBON LOW-ALLOY STEEL (BW BL 50CRMO4) AT ARCELORMITTAL TUBARÃO AND WAELZHOLZ BRASMETAL LAMINAÇÃO FOR DIRECT APPLICATION IN CHAINSAW GUIDEBAR

NOVOS AÇOS ALTERNATIVOS ESTÃO SENDO CONTINUAMENTE PROPOSTOS PARA REDUZIR CUSTOS E MELHORAR A COMPETITIVIDADE DO SETOR. ESTE ESTUDO APRESENTA O DESENVOLVIMENTO DO AÇO DE ALTO CARBONO BAIXA LIGA, BW BL 50CRMO4, NA ARCELORMITTAL TUBARÃO E NA WAELZHOLZ BRASMETAL LAMINAÇÃO, COMO PRODUTO RELAMINADO PARA ATENDER AS DEMANDAS DO MERCADO DE SABRES E FERRAMENTAS DE MOTOSSERRA, FORNECENDO UM PRODUTO PRONTO PARA USAR DIRETAMENTO E REDUZIR AS ETAPAS DO TRATAMENTO TÉRMICO DO CLIENTE FINAL. A PRODUÇÃO DESTE TIPO DE AÇO REQUER RIGOROSO CONTROLE DE PROCESSO DESDE A AÇORIA ATÉ A RELAMINAÇÃO. ESTE AÇO É AMPLAMENTE UTILIZADO EM COMPONENTES QUE REQUEREM ALTA RESISTÊNCIA MECÂNICA, LIMPIDEZ, MANUTENÇÃO DE FORMA E RESISTÊNCIA À ABRASÃO. ESTE ESTUDO INVESTIGOU, EM ESCALA INDUSTRIAL, OS PARÂMETROS DO PROCESSO E CARACTERÍSTICAS CRÍTICAS PARA O DESENVOLVIMENTO DE UMA CHAPA DE AÇO DE ALTO CARBONO COM LIGA CR E MO PARA SABRE DE MOTOSSERRA. O AÇO FOI CARACTERIZADO DURANTE TODO O PROCESSO (LINGOTAMENTO CONTÍNUO, LAMINAÇÃO A QUENTE, LAMINAÇÃO A FRIO + RECOZIMENTO DE LOTE E TRATAMENTO TÉRMICO) UTILIZANDO TESTES DE TRAÇÃO, TESTES DE DUREZA, MICROSCOPIA ÓPTICA (OM) E MICROSCOPIA ELETRÕ ÔNICA DE VARREDURA (MEV). OS RESULTADOS MOSTRARAM A EVOLUÇÃO DA MICROESTRUTURA DO MATERIAL, DESDE UMA MICROESTRUTURA DE FERRITA/PEARLITA LAMINADO A QUENTE, ESFEROIDIZADA EM LAMINAÇÃO A FRIO + RECOZIMENTO, ATÉ UMA MICROESTRUTURA TOTALMENTE BAINÍTICA APÓS AUSTEMPERA, PRONTA PARA A FABRICAÇÃO DE SABRES DE MOTOSSERRA.

NEW ALTERNATIVE STEELS ARE CONTINUALLY FREQUENTLY BEING PROPOSED TO REDUCE COSTS AND IMPROVE INDUSTRY COMPETITIVENESS. THIS STUDY PRESENTS THE DEVELOPMENT OF HIGH-CARBON LOW-ALLOY STEEL, BW BL 50CRMO4, AT ARCELORMITTAL TUBARãO AND WAELZHOLZ BRASMETAL LAMINAçãO, AS A RE-ROLLED PRODUCT TO MEET THE DEMANDS OF THE CHAINSAW BAR AND TOOL MARKET, PROVIDING A READY-TO-USE PRODUCT AND REDUCING THE FINAL CUSTOMER'S HEAT TREATMENT STEPS. THE PRODUCTION OF THIS TYPE OF STEEL REQUIRES RIGOROUS PROCESS CONTROL FROM THE STEEL MILL TO THE RE-ROLLING. THIS STEEL IS WIDELY USED IN COMPONENTS THAT REQUIRE HIGH MECHANICAL STRENGTH, CLEANLINESS, SHAPE MAINTENANCE, AND ABRASION RESISTANCE. THIS STUDY INVESTIGATED, ON AN INDUSTRIAL SCALE, THE PROCESS PARAMETERS, AND CRITICAL CHARACTERISTICS FOR DEVELOPING A HIGH-CARBON STEEL SHEET WITH CR AND MO ALLOY FOR CHAINSAW GUIDEBAR. THE STEEL WAS CHARACTERIZED THROUGHOUT THE ENTIRE PROCESS (CASTING, HOT ROLLING, COLD ROLLING + BATCH ANNEALING, AND HEAT TREATMENT) USING TENSILE TESTING, HARDNESS TESTING, OPTICAL MICROSCOPY (OM), AND SCANNING ELECTRON MICROSCOPY (SEM). THE RESULTS SHOWED THE EVOLUTION OF THE MATERIAL'S MICROSTRUCTURE, FROM A FERRITE/PEARLITE MICROSTRUCTURE ON THE HOT BAND, SPHEROIDIZED IN COLD ROLLING + ANNEALING, TO A FULLY BAINITIC MICROSTRUCTURE AFTER AUSTEMPERING, READY FOR THE MANUFACTURE OF CHAINSAW BARS.

Keywords

AÇO DE ALTO CARBONO; GUIA DE MOTOSSERRA; TUBARÃO ARCELORMITTAL; WAELZHOLZ BRASMETAL LAMINAÇÃO.

High-carbon steel; chainsaw guidebar; ArcelorMittal Tubarão; Waelzholz Brasmetal Laminação.

How to refer

JESUS, HENRIQUE SEVERIANO DE; FERREIRA, FERNANDO GENEROSO NEIVA; MACHADO, EDUARDO ALVES; BARBOSA, FABIANO ALMIR; POSSATI, JULIANO BRAZ; RODRIGUES, MARCELO URDAPILLETA; BOMFIM, MAURÍCIO FRANCO; BARROSO, MARINA DE LIMA; FERRO, DANIEL AUGUSTO; FRANK, THOMAS. DESENVOLVIMENTO DE AÇO ALTO CARBONO BAIXA LIGA (BW BL 50CRMO4) NA ARCELORMITTAL TUBARÃO E WAELZHOLZ BRASMETAL LAMINAÇÃO PARA APLICAÇÃO DIRETA EM SABRE DE MOTOSSERRA , p. 541-551. In: _FAUT, São Paulo, 2000.
ISSN: - , DOI 10.5151/Fault-41174